GLASS AS A BUILDING MATERIAL
Submitted by: komal kumari
Submitted to: Proff. Rohini Kushwaha
Table Of Content o o o o o o o o o o
Introduction History of glass Pilkington manufacturing process Properties of glass Composition of glass Specifications for glass Glass Mulching Glass Sculpture Advantages Of Glass Disadvantages Of Glass
Introduction Glass is a material made from liquid sand. It is the name given to any amorphous (non-crystalline) solid that displays a glass transition near its melting point which is around 1,700°C (3,090°F). This means that materials transform from a hard and brittle state into a molten state, or vice versa depending on whether the glass transition temperature is the melting or solidifying point. An amorphous solid has some of the crystalline order of a solid and some of the random molecular structure of a liquid.
Silicate glass is the most common form, which consists mainly of silica or silicon dioxide, SiO2. Impurities or additional elements and compounds added to the silicate to change the color and other properties of the glass. glass is a very commonly used material because, whilst still molten, it can be manipulated into forms suitable for a very wide range of different uses, from packaging and household objects to car windscreen, windows, and so on.
History Of Glass Archaeological evidence has been found of man-made glass dating back to 4000 BC in the form of decorative glazes. In prehistoric times, weapons were made using obsidian and fulgurite, naturally occurring glasses found in volcanic regions and after lightning strikes respectively. Around 1500 BC glass was first used as a material for making hollow containers. The Romans excelled at glassmaking and were responsible for introducing it to Britain. Although very guarded over the secrets of glassmaking, when the Roman Empire fell, the skills proliferated throughout Europe and the Middle East. Glass was popularized as a technical building material by Joseph Paxton’s Crystal Palace at the Great Exhibition of 1851. Since that period, glass manufacturing techniques have developed considerably with advancements in science and technology. In 1958, Pilkington and Bickerstaff introduced a commercial float glass process, a method that would revolutionize glass manufacturing. Their method gave glass sheets uniform thickness and very flat surfaces, precisely the characteristics that mean nearly all modern windows are made from float glass.
Pilkington manufacturing process The Pilkington process for manufacturing glass involves the following basic stages:
Raw materials (clear sand, calcium oxide, sodium carbonate) are weighed and mixed proportionally along with the addition of admixtures to provide specific technical or visual properties. The mixture is heated in a gas-fired furnace or electric smelter, pot furnace or kiln. Molten glass is formed at around 1700°C (3090°F) and is floated on molten tin to form glass of the desired thickness. The glass is cooled, the precise process determining its overall strength.
Properties of glass The composition of glass and the cooling rate can be varied to give a range of
the end use required:
properties depending on
Visual transparency and reflectance can be altered with the addition of admixtures to the initial batch mix. Glass can be transparent, translucent, tinted, reflective, stained, opaque, and so on. Solar optical properties can be controlled to transmit, absorb or reflect specific wavelengths of the solar spectrum.
Long wave infra-red optical properties can be varied to affect emissivity, for example to create low-e glass. U value can be altered by the R-value of layers of glass and their surface heat transfers. Strength can be altered with laminates and admixtures that increase the ability of glass to resist deformation, shearing or shattering under load. Glass can be worked in many different ways, from blowing, drawing and pressing to welding. Glass is 100% recyclable. Scraps of waste glass are used as raw materials in glass manufacture and as aggregates in concrete manufacture. The number of times glass has been recycled does not affect its quality, strength or functionality.
Composition of glass • There are many different types of glass, each with different chemical and physical properties dependent upon their application. The main types of glass include: • Borosilicate glass • Made of 70-80% silica, 7-13% boric oxide, smaller amounts of alkalis and aluminum oxide. Widely used by the chemical and pharmaceutical industries as well as for common household items, under the trade name Pyrex. • Commercial glass • This is the most common type of glass, made primarily from sand. As it is normally colorless, this glass is popularly used for windows. • Glass fiber • The composition of glass fiber varies according to its application. For building insulation, the glass used is normally soda lime, whereas for textiles, an alumino-borosilicate glass with very low sodium oxide content is preferred because of its good chemical durability. • Lead glass • This is used to make predominately decorative glass objects. Calcium oxide is replaced by lead oxide, and potassium oxide replaces all or a high proportion of the sodium oxide. Lead glass sparkles brightly and has a relatively soft surface, both properties that make it so suitable for decorative uses.
Specifications for glass Float glass This is named after the modern process used to create large, thin, flat panels from molten glass which is floated onto a pool of molten metal such as tin. This process produces a very smooth sheet of glass with a highly consistent thickness. Annealed glass This is a piece of float glass that has been cooled in a slow and controlled manner. The internal stresses within the sheet of glass are reduced by this process making the resulting glass stronger and less likely to break than it would otherwise be. There can be safety concerns using annealed glass as it can break into large jagged shards. Heat strengthened glass This is made from a sheet of annealed glass reheated beyond its annealing point of around 1,200ºF and then cooled slowly. Heat strengthened glass may be twice as strong as annealed glass, but may still need to be laminated for use in buildings.
Fully tempered glass Tempering is the process by which annealed glass is heated in the same way as heat strengthened glass. The glass is cooled more rapidly which allows the internal portion of the glass to remain fluid for longer than the outer surfaces. This means that an equal amount of tensile and compressive stresses are formed across the glass which allows it to become in the order of four times as strong as annealed glass. This is used as a safety glass, as it shatters into small granular pieces rather than sharp shards, reducing the risk of injury. Heat soaked tempered glass This is used as a means of testing glass panes that are to be used in safety critical situations, such as a glass railing. Tempered glass panes are heated to a temperature of around 550ºF for a few hours. This causes any unstable nickel sulfide inclusions (imperfections that may cause spontaneous breakage of the pane) to expand disproportionately to the glass, making the glass break. Laminated glass Laminated glass is used where glazing must remain intact if it is broken, either for safety or security reasons. It is made by fusing two or more layers of glass with interlayers of polyvinyl butyral (PVB) through the use of heat and pressure. If it is made using heat strengthened glass, the pane will break into large pieces but will be held in the frame by the PVB inter-layer. If it is made from tempered glass, the sheet may fall out of the frame but will mostly stay together due to the inter-layer.
Wired glass This is most often used as a fire resistant glass because the wire holds the glass in place if high temperature causes it to break. The wire mesh is better at holding glass in place than the PVB films used in laminated glass. Low-emissivity (Low-E) glass The term ‘low-e glass’ is used to describe glass that has a coating added to one or more of its surfaces to reduce its emissivity so that it reflects, rather than absorbs, long-wave infrared radiation. In cooler climates this means that long-wave infra-red radiation that builds up inside a building is reflected by the glass back into the space, rather than being absorbed by the glass and then partially re-radiated to the outside. This reduces heat loss and so the need for artificial heating. In hotter climates, a low-e coating means that long-wave infra-red radiation outside the building is reflected back out of the building, rather than being absorbed by the glass and then partially reradiated to the inside. This reduces the heat build-up inside the building and so the need for cooling. In hotter climates, a low-e coating might be used in conjunction with solar-control glass to reduce the amount of short-wave solar radiation entering the building. The two main types of low-e coating are tin and silver. Tin oxide is applied to the glass at high temperatures to create a very hard and durable low-e coating. Silver coating must be enclosed within the glazing unit so that oxidation doesn’t cause the degradation of the silver over time.
Self cleaning glass A transparent coating can be applied to glass during the manufacturing which reacts with the sun’s UV rays to break down dirt and grime which forms on the outside of the windows, and when it rains, the decomposed dirt natural rinses away. The coating has hydrophilic properties which mean it attracts water over its entire surface, avoiding unsightly uneven water marks.
Glass Mulching Vibrant colours that won’t fade or need replacing Glass mulches are a unique, low- maintenance alternative to traditional bark or gravel mulches Environmentally-friendly, green landscaping Adds beauty and character to any outdoor entertainment area Clean alternative to logs or lava rocks Lasts a lifetime without ever burning, melting or discolouring Enhance your backyard landscape Customize your fire pit to compliment your taste GLASS MULCHES
Glass Sculpture
Advantages Of Glass • The glass that absorb, refracts or transmits light. It can be made transparent or translucent so it adds extraordinary beauty to the building . • Glass transmits up to 80% of available natural day light in both directions without any yellowing, clouding or weathering . • The glass is fully weather resistance so it can withstand the effects of the wind, rain, or the sun and can retain its appearance and integrity. • Glass does not rust so it does not degrade gradually by chemical and surrounding environment effects. • Glass has a smooth glossy surface so it is dust proof and can be easily cleaned. • Glass allows natural light to enter the house even if doors/windows are closed so thus it saves energy and also lowers the electricity bills, brightens up the room and brings out the beauty of the homeland most importantly it boosts the mood of occupant. • It is an excellent insulator against electricity. It is impossible to conduct an electric current under the influence of an electric field. • Available in varieties of colors and when we combine the glass sheet in laminated or insulated units, they change in color and appearance.
• Glass is 100% recyclable and it does not degrade during the recycling process, hence it can be recycled again and again without loss of quality or purity. • The glass is excellent abrasion resistant so it will resist surface wear caused by flat rubbing and contact with another material. • It is unaffected by noise, air, water and most of the acids hence discoloration, alteration in the degree of shine, softening, swelling, the detachment of coatings and blistering will not occur. Glass also protects against outside barriers. • Glass has the ability to make the structure look more stunning, sophisticated and adds beauty to the building. It is used to achieve the architectural view for external decoration. • When used in the interiors, glass saves space.
Disadvantages Of Glass • Manufacturing of glass is high energy consuming process due to high temperature required for processing the raw materials, and it is expensive material and ultimately increases the cost of a building. • The glass is very rigid and brittle materials so when it is subjected to stress, it breaks without significant (strain). Broken pieces of Glass may be sharp and chances of injury are very high. • The glass is less impact resistant so the capability of the glass to withstand a suddenly applied load is very poor. • The glass is affected by external hydrofluoric acid hence sometime etching is appear on glass surface. • The Glass is affected by alkalis ions. Alkali solution simply dissolves a glass surface and as long as the supply of alkali is sufficient, this type of corrosion takes place at a uniform rate. • Glass offers superior transparency of heat hence it is to be balanced with its relatively low R-value (energy saving). R-value is considered as one of the most important factors for insulating. • Use of glass also enhances the cost of security.
•The glass is also unsafe for earthquake proven area. Unfortunately, there is no such Glass as an earthquake proof material but costly treatment makes them withstand against earthquake. • The glass is poor in terms of heat preservation, leading to higher costs in the operation of air-conditioners. • Though many feel that once you provide glass in a building façade, you are free from painting expenses for ever but this is not fine. You may have to spend equally for cleaning of glass. Sometimes it is as costly as expose painting. Again, you may paint building once in a 5 years but for glass you have to clean every year. • Glass absorbs heat and hence act as a greenhouse and hence not suitable in warm and hot climates. It will increase AC load and more energy consideration for air conditioning. • Glare is a major problem in glass façade building.